Spin-to-charge conversion is an essential requirement for the implementation of spintronic devices. Recently, monolayers (MLs) of semiconducting transition-metal dichalcogenides (TMDs) have attracted considerable interest for spin-to-charge conversion due to their high spin-orbit coupling and lack of inversion symmetry in their crystal structure. However, reports of direct measurement of spin-to-charge conversion at TMD-based interfaces are very much limited. Here, we report on the room-temperature observation of a large spin-to-charge conversion arising from the interface of Ni80Fe20 (Py) and four distinct large-area (∼5 × 2 mm2) ML TMDs, namely, MoS2, MoSe2, WS2, and WSe2. We show that both spin mixing conductance and the Rashba efficiency parameter (λIREE) scale with the spin-orbit coupling strength of the ML TMD layers. The λIREE parameter is found to range between -0.54 and -0.76 nm for the four ML TMDs, demonstrating a large spin-to-charge conversion. Our findings reveal that the TMD/ferromagnet interface can be used for efficient generation and detection of spin current, opening new opportunities for novel spintronic devices.
Keywords: ferromagnetic resonance; inverse Rashba Edelstein effect; spin pumping; spin-to-charge conversion; transition-metal dichalcogenides.