Defect management by a cesium fluoride-modified electron transport layer promotes perovskite solar cells

Xiangning Xu; Zhichao Lin; Qingbin Cai; Hongye Dong; Xinli Wang; Cheng Mu

doi:10.1039/d2cp03207d

Defect management by a cesium fluoride-modified electron transport layer promotes perovskite solar cells

Phys Chem Chem Phys. 2022 Sep 28;24(37):22562-22571. doi: 10.1039/d2cp03207d.

Authors

Xiangning Xu¹, Zhichao Lin¹, Qingbin Cai¹, Hongye Dong¹, Xinli Wang¹, Cheng Mu¹

Affiliation

¹ Key Laboratory of Advanced Light Conversion Materials and Biophotonics, Department of Chemistry, Renmin University of China, Beijing, 100872, P. R. China. cmu@ruc.edu.cn.

PMID: 36102344
DOI: 10.1039/d2cp03207d

Abstract

SnO₂ is a candidate material for electron transport layers (ETLs) in perovskite solar cells (PSCs). However, a large number of defects at the SnO₂/perovskite interface lead to notable non-radiative interfacial recombination. Moreover, the energy level arrangement between SnO₂/perovskite does not match well. In this study, a SnO₂/CsF-SnO₂ double-layer ETL was prepared by doping CsF into SnO₂, effectively passivating the defects of the SnO₂ ETL and SnO₂/perovskite interface. The formation of a good energy level arrangement with the perovskite layer reduces the interface non-radiative recombination and improves the performance of the interface charge extraction. The photoelectric conversion efficiency of the optimal CsF-modified PSC reached 22.18%, owing to the significant increase in the open-circuit voltage to 1.180 V.