Ionic Polymer Metal Composites (IPMCs) are in high demand owing to the ongoing advancements in technology for various applications. New fabrication techniques and a quick retort towards the applied load are the significant reasons for considering IPMCs in smart devices. Here, a Teflon fabric-reinforced Nafion (TFRN) membrane is used to create an IPMC. The materials employed as electrodes are silver and nanofillers. The basement membrane, Nafion 438 (N-438), is sandwiched between the electrodes using a chemical decomposition technique. Subsequently, the electromechanical properties (actuation) of the membrane are tested. The micro and molecular structure of the IPMC membrane coated with Silver (Ag), Ag-Carbon nanotubes (CNTs), and Ag-Graphene nanoparticles samples are examined with the help of SEM and X-ray diffraction (XRD). The membrane scratch test is carried out to evaluate the abrasion and wear resistance of the membrane. The lowest coefficient of friction is shown by N438 + Ag + Graphene (0.05), which increased by 300% when compared to a pure N438 membrane. The hydration and tip deflection test were also performed to understand the water uptake percentage. At 90 °C, the highest water uptake was observed for N438 + Ag + Graphene (0.05), which decreased by 60, 42, 23, 14 and 26% when compared to N438, N438 + Ag, N438 + Ag + CNT (0.01), N438 + Ag + CNT (0.05) and N438 + Ag + Graphene (0.01), respectively. A proportional relationship between hydration level and tip deflection is observed and the highest bending performance is observed for the N438 + Ag + Graphene (0.05) membrane.
Keywords: CNT; Nafion; graphene; ionic polymer metal composites.