Purpose: To investigate the bond durability of composite cement to zirconia after treatment with a 15-methacryloyloxypentadecyl dihydrogen phosphate (15-MPDP)-containing adhesive and 2 commercially available adhesives.
Materials and methods: Ninety zirconia bars were fabricated and bonded to prepolymerized resin composite cylinders with a composite cement after surface treatment for 20 s using the following adhesives: Adper Easy One (AEO, negative control), Single Bond Universal (SBU, positive control), and 10 wt% 15-MPDP powder mixed with Adper Easy One (15- MPDP). After storage in distilled water at 37°C for 24 h, the specimens were divided into 3 subgroups according to the aging treatment applied (n = 10): no aging treatment (0/TC), 10,000 thermocycles (1/TC), and 37,500 thermocycles (3/TC). Shear bond strength (SBS) was analyzed using two-way ANOVA (p < 0.05), and the fracture surfaces were examined under a dental microscope.
Results: Significant differences in the SBSs among the surface treatments and aging treatments were observed (both p < 0.001). The 15-MPDP and SBU groups showed significantly higher SBSs than the AEO group, whereas similar SBSs were found in the 15-MPDP and SBU groups. Significant reductions in the SBSs were found after 37,500 thermocycles (p < 0.001), although no significant difference between specimens aged with 10,000 thermocycles and non-aged specimens was observed.
Conclusions: The 15-MPDP-containing dental adhesive exhibited bond durability comparable to that of a well-established 10-MDP-containing universal adhesive. Aging by 10,000 thermocycles may be insufficient to disrupt the bond of composite cement to zirconia.
Keywords: 10-MDP; 15-MPDP; shear bond strength; thermocycling; zirconia bonding.