How does the occlusal contact region influence the mechanical fatigue performance and fracture region of monolithic lithium disilicate ceramic crowns?

Abstract

Objective: To characterize the effect of the occlusal contact region on the mechanical fatigue performance and on the fracture region of monolithic lithium disilicate ceramic crowns.

Materials and methods: Monolithic lithium disilicate ceramic crowns were machined in a CAD/CAM system and adhesively luted onto glass-fiber reinforced epoxy resin preparations with resin cement. The crowns were divided into three groups (n = 16) according to load application region (cusp tip: restricted to cusp tips; cusp plane: restricted to cuspal inclined plane; or mixed: associating tip cusp and cuspal inclined plane). The specimens were submitted to a cyclic fatigue test (initial load: 200 N; step-size: 100 N; cycles/step: 20,000; loading frequency: 20 Hz; load applicator: 6 mm or 40 mm diameter stainless steel) until observing cracks (1st outcome) and fracture (2nd outcome). The data were analyzed by the Kaplan-Meier + Mantel-Cox post-hoc tests for both outcomes (cracks and fracture). Finite element analysis (FEA), occlusal contact region, contact radii measurements, and fractographic analyzes were performed.

Results: The mixed group presented worse fatigue mechanical behavior (550 N / 85.000 cycles) compared to the cuspal inclined plane group (656 N / 111,250 cycles) (p < 0.05) for the first crack outcome, while the cusp tip group was similar to both groups (588 N / 97,500 cycles) (p > 0.05). The mixed group had the worst fatigue behavior (1413 N / 253,029 cycles) in relation to the other groups (Cusp tip: 1644 N / 293,312 cycles; Cuspal inclined plane: 1631 N / 295,174 cycles) considering the crown fracture outcome (p < 0.05). FEA showed higher tensile stress concentration areas just below the load application region. In addition, loading on the cuspal inclined plane induced a higher tensile stress concentration in the groove region. The most prevalent type of crown fracture was the wall fracture. Groove fracture was observed in 50% of the loading specimens exclusively on the cuspal inclined plane.

Conclusion: Load application on distinct occlusal contact regions affects the stress distribution pattern and consequently the mechanical fatigue performance and fracture region of the monolithic lithium disilicate ceramic crowns. A combination of loading at distinct regions is recommended to promote better evaluation of the fatigue behavior of a restored set.

Keywords: Dental ceramics; Fatigue; Fracture; Loading pattern.