A photodetector based on a hybrid dimensional heterostructure of laterally aligned multiwall carbon nanotubes (MWCNTs) and multilayered MoS2 was prepared using the micro-nano fixed-point transfer technique. Thanks to the high mobility of carbon nanotubes and the efficient interband absorption of MoS2, broadband detection from visible to near-infrared (520-1060 nm) was achieved. The test results demonstrate that the MWCNT-MoS2 heterostructure-based photodetector device exhibits an exceptional responsivity, detectivity, and external quantum efficiency. Specifically, the device demonstrated a responsivity of 3.67 × 103 A/W (λ = 520 nm, Vds = 1 V) and 718 A/W (λ = 1060 nm, Vds = 1 V). Moreover, the detectivity (D*) of the device was found to be 1.2 × 1010 Jones (λ = 520 nm) and 1.5 × 109 Jones (λ = 1060 nm), respectively. The device also demonstrated external quantum efficiency (EQE) values of approximately 8.77 × 105% (λ = 520 nm) and 8.41 × 104% (λ = 1060 nm). This work achieves visible and infrared detection based on mixed-dimensional heterostructures and provides a new option for optoelectronic devices based on low-dimensional materials.
Keywords: heterostructures; mixed dimensions; molybdenum disulfide; oriented multi-walled carbon nanotubes; photodetectors.