Despite the unique features of poly-L-lactic acid (PLLA), its mechanical properties, such as the elongation at break, need improvement to broaden its application scope. Herein, poly(1,3-propylene glycol citrate) (PO3GCA) was synthesized via a one-step reaction and evaluated as a plasticizer for PLLA films. Thin-film characterization of PLLA/PO3GCA films prepared via solution casting revealed that PO3GCA shows good compatibility with PLLA. The addition of PO3GCA slightly improves the thermal stability and enhances the toughness of PLLA films. In particular, the elongation at break of the PLLA/PO3GCA films with PO3GCA mass contents of 5%, 10%, 15%, and 20% increases to 172%, 209%, 230%, and 218%, respectively. Therefore, PO3GCA is promising as a plasticizer for PLLA.
Keywords: citric acid; poly(1,3-propylene glycol); polylactic acid; toughening agent.