The "solvent-in-salt" electrolytes for an aqueous system, including "water-in-salt" electrolytes and "bisolvent-in-salt" electrolytes, have shown significantly improved electrochemical stability toward low-voltage anodes and high-voltage cathodes. However, the heavy use of salt raises concerns of high cost, high viscosity, inferior wettability, and poor low-temperature performance. Herein, a "localized bisolvent-in-salt electrolyte" is proposed by introducing 1,1,2,2-tetrafluoroethyl-2,2,3,3-tetrafluoropropyl ether (TTE) as the diluent to the high-concentration water/sulfolane hybrid (BSiS-SL) electrolytes, forming a ternary solvent-based electrolyte, Li(H2O)0.9SL1.3·TTE1.3 (HS-TTE). The introduction of TTE dilutes the compact ionic clusters, while the original primary Li+ solvation structure remains, and in the meantime, boosts the formation of a robust solid electrolyte interphase. As a result, a wide electrochemically stable window of 4.4 V is achieved. In comparison with the bisolvent BSiS-SL system, the trisolvent HS-TTE electrolyte exhibits a low salt concentration of 2.1 mol kg-1, resulting in drastically reduced viscosity, superb separator wettability, and largely improved low-temperature performance. The constructed 2.5 V Li4Ti5O12/LiMn2O4 cell shows an excellent capacity retention of 80.7% after 800 cycles, and the cell can even work at -30 °C. With these extraordinary advantages, the fundamental designing strategy of the HS-TTE electrolyte developed in this work can promote the practical applications of solvent-in-salt electrolytes.
Keywords: electrochemically stable window; localized bisolvent-in-salt electrolyte; solid electrolyte interphase; solvent-in-salt electrolytes; water/organic hybrid electrolyte solvation structures.