Tritan™ (a kind of glycol-modified polycyclohexylene dimethylene terephthalate) is a novel copolyester mainly in use for the production of sports bottles and food storage containers. Oligomers in three food-grade Tritan™ samples were identified after dissolution-precipitation by high performance liquid chromatography with diode array detection and mass spectrometry and quantified after alkaline hydrolysis to the monomers. The obtained overall oligomer content <1000 Da determined by hydrolysis ranged from 7.2 to 10.6 mg/g material. Three consecutive migration experiments were performed according to the Commission Regulation (EU) No 10/2011. Oligomer migration values decreased from first to third migration during all simulations. Less than 25 µg/kg (third migrate) were detected in bottle migrates when tested under room temperature storage conditions (40 °C, 24 h) with simulants 3% acetic acid, 20 and 50% ethanol and during hot-fill testing (70 °C, 2 h) with simulants 3% acetic acid and 20% ethanol, respectively, while 170 µg/kg were determined in 50% ethanol after migration at 70 °C for 2 h. Food storage containers that were labelled as microwave-suitable by the supplier were tested according to the Joint Research Centre recommendations for microwave dishware. A strong deformation of the containers as well as a loss of transparency were observed during the tests (100 °C, 2 h with 10% ethanol and 3% acetic acid in an autoclave, 121 °C, 30 min with sunflower oil), questioning the suitability of the material for microwave applications. Maximum oligomer migration was 379 µg/kg during the third migration (sunflower oil at 121 °C for 30 min). Based on the migration data and an in silico oligomer evaluation according to the threshold of toxicological concern concept, no exceedances of daily thresholds for oligomers are expected from a proper use of Tritan™ drinking bottles, even with hot drinks.
Keywords: Exposure; food contact materials; food simulants; migration; oligomers.