Transparent microelectrodes that facilitate simultaneous optical and electrophysiological interfacing are desirable tools for neuroscience. Electrodes made from transparent conductors such as graphene and indium tin oxide (ITO) show promise but are often limited by poor interfacial charge-transfer properties. Here, microelectrodes are demonstrated that take advantage of the transparency and volumetric capacitance of the mixed ion-electron conductor Poly(3,4- ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS). Ring-shaped microelectrodes are fabricated by inkjet-printing PEDOT:PSS, encapsulating with Parylene-C, and then exposing a contact site that is much smaller than the microelectrode outer diameter. This unique structure allows the encapsulated portion of the microelectrode volume surrounding the contact site to participate in signal transduction, which reduces impedance and enhances charge storage capacity. While using the same 100 μm diameter contact site, increasing the outer diameter of the encapsulated electrode from 300 to 550 μm reduces the impedance from 294±21 to 98±2 kΩ, respectively, at 1 Hz. Similarly, the charge storage capacity is enhanced from 6 to 21 mC cm-2. The PEDOT:PSS microelectrodes provide a low-haze, high-transmittance optical interface, demonstrating their suitability for optical neuroscience applications. They remain functional after a million 1 V stimulation cycles, up to 600 μA of stimulation current, and more than 1000 mechanical bending cycles.
Keywords: PEDOT:PSS; impedance modeling; printing; transparent microelectrodes; volumetric capacitance.