In this work, we investigated in detail the upconversion properties of several types of nanoparticles, including NaYF4:5%Yb3+/30%Mn2+, NaYF4:40%Mn2+/x%Yb3+ (x% = 1, 5, 10, 20, 30, and 40), NaYF4:2%Er3+/x%Mn2+ (x% = 20, 30, 40, 50, 60, and 70), NaYF4:40%Mn2+/x%Er3+ (x% = 1, 2, 5, and 10), and NaYF4:40%Mn2+/1%Yb3+/x%Er3+ (x% = 0, 2, 5, and 10). We studied their upconversion emission under 980 nm excitation in both pulsed and continuous wave modes at different synthesis temperatures. The nanoparticles were characterized using transmission electron microscopy (TEM), X-ray diffraction (XRD), and photoluminescence (PL) spectroscopy. The doping of Yb3+ and Mn2+ ions resulted in the nanoparticles assuming cubic and hexagonal crystal structures. The emission intensity increased (106.4 (a.u.*103) to 334.4(a.u.*103)) with increasing synthesis temperature from 120 to 140 °C, while a sharp decrease was observed when the synthesis temperature was increased to 200 °C. The gradual decrease in peak intensity with increasing Mn2+ concentration from 20 to 70% was attributed to energy transfer from Mn2+ to Yb3+. In NaYF4:Mn2+/Yb3+/Er3+ UCNPs, increasing the Er3+ concentration from 0 to 10% led to the disappearance of the blue, orange, and green emission bands. The intense upconversion luminescence pattern with high spatial resolution indicates excellent potential for applications in displays, biological sensors, photodetectors, and solar energy converters.
© 2023. Springer Nature Limited.