In Bolivia, lateritic soils are common in humid tropical regions and can be used in the construction industry as an alternative to materials that cause a negative environmental impact, such as cement. The production of Portland cement causes environmental issues like significant greenhouse gas emissions and air pollution. To address this problem, geopolymers have been introduced as an alternative binder with low CO2 emissions. In this regard, geopolymers based on lateritic clays have been studied mineralogically, chemically, and on their compressive strength separately. However, there are still no studies on lateritic clays present in Bolivia and their mechanical, mineralogical, and chemical properties combined in a geopolymer. Therefore, this present research proposes the evaluation of a geopolymer made from laterite clays. Compression and flexural tests were carried out, along with mineralogical and chemical analyses on mortar and geopolymer cubes and prisms. The results indicate that the laterite clay-based geopolymer has lower compressive strength compared to Portland cement IP (cement type I with the addition of pozzolana) mortar. However, the flexural strength tests show a slight increase in the case of the geopolymer.
Keywords: Portland cement; bending strength; compressive strength; geopolymer; lateritic soil.