Aim: To evaluate the push-out bond strength of two newly modified mineral trioxide aggregates (MTAs) with conventional MTA and biodentine.
Materials and methods: Material preparation: Two commercially available bioactive bioceramics: Group I: Mineral trioxide aggregate; Group II: Biodentine; and two newly formulated modified MTAs: Group III: Doxycycline incorporated MTA formulation; Group IV: Metronidazole incorporated MTA formulation was used in the present study. All the test materials were then carried using a plastic instrument to the desired experimental design. Teeth sample preparation: A total of 120 teeth samples were collected and divided into four groups of test materials with 30 teeth samples per group. Single-rooted permanent teeth, that is, incisors were collected and stored in saline until the study was performed. Sectioning of the teeth into 2.0 ± 0.05-mm thick slices was performed perpendicular to the long axis of the tooth. The canal space was instrumented using Gates Glidden burs to achieve a diameter of 1.5 mm. All four prepared materials were mixed and placed in the lumen of the slices and placed in an incubator at 37°C for 72 hours. Push-out test and bond failure pattern evaluation: The push-out test was performed using a universal testing machine. The slices were examined under a scanning electron microscope (SEM) at 40× magnification to determine the nature of bond failure. All the collected data were recorded and statistically analyzed.
Results: The mean push-out bond strength was found to be the highest for group II (37.38 ± 1.94 MPa) followed by group III (28.04 ± 2.22 MPa) and group IV (27.83 ± 1.34 MPa). The lowest mean push-out bond strength was noticed with group I (22.89 ± 2.49 MPa). This difference was found to be statistically significant (p = 0.000). Group I samples had the predominantly adhesive type of failure (86.4%), while group II samples showed the cohesive type of failure (94.2%). Both the modified MTAs (groups III and IV) primarily showed mixed types of failures.
Conclusion: Both the antibacterial-enhanced MTAs had better pushout bond strength compared to conventional MTA but did not outperform biodentine. Hence, it could serve as a substitute for conventional MTA due to its augmented physical properties.
Clinical significance: Carious pulp exposure and nonvital open apices pose a critical challenge to pediatric dental practitioners. In such circumstances, maintaining the vitality of pulp and faster healing would help in a better prognosis. Novel MTAs without any cytotoxic components, and enhanced antibacterial contents with augmented physical properties can help in treating such clinical conditions. How to cite this article: Merlin ARS, Ravindran V, Jeevanandan G, et al. Comparative Evaluation of Push-out Bond Strength of Conventional Mineral Trioxide Aggregate, Biodentine, and Two Novel Antibacterial-enhanced Mineral Trioxide Aggregates. J Contemp Dent Pract 2024;25(2):168-173.
Keywords: Antibacterial-enhanced mineral trioxide aggregate; Biodentine; Dental; Disease; Doxycycline Metronidazole..