The reuse and development of natural waste resources is a hotspots and challenges in the research of new fiber materials and the resolution of environmental concern globally. Herein, this study aimed to develop a simple and direct manual extraction process to extract Musa core fibers (MCFs) for rapid water conduction and evaporation. Through simple processes such as ring cutting and stretching, this green and non-destructive inside-out extraction strategy enabled Musa fibers to be naturally and harmlessly degummed from natural Musa stems, with good maintenance of the fiber structure and highly helical morphology. The extracted fibers are composed of regularly and closely arranged cellulose nanofibrils in the shape of ribbon spirally arranged multi-filaments, and the single filament is about 2.65 μm. The high-purity fibers exhibit ultra-high tensile strength under a non-destructive extraction process, and the ultimate tensile strength in dry state is as high as 742.95 MPa. The tensile strength is affected by the number of fiber bundles, which shows that tensile strength and tensile modulus is higher than those of vascular bundle fibers in dry or wet condition. In addition, the MCFs membrane indicates good water conductivity, with a water absorption height of 50 mm for the sample in only 60 s. Moreover, the water evaporation rate of MCFs reaches 1.37 kg m-2 h-1 in 30 min, which shows that MCFs have excellent water conductivity and evaporation rate compared with ordinary cotton fibers. These results indicate that MCFs have great potential in replacing the use of chemical methods to extract fibers from vascular bundles, providing an effective way to achieve sustainability in quick-drying applications, as well as in the sustainable development of natural waste resources.
Keywords: Biological structure; Mechanical performance; Musa stem; Vascular bundles; Wicking and water evaporation.
Copyright © 2024. Published by Elsevier B.V.