Photothermal synergistic catalysis is a novel technology that converts energy. In this study, ZnIn2S4 with S-vacancy (ZIS-Vs) is combined with Nickel, Nickle Oxide and Carbon Nanofiber aggregates (Ni-NiO@CNFs) to create a multi-interface coupled photocatalyst with double Schottky barrier, double channel and mixed photothermal conversion effect. Theoretical calculation confirms that the Gibbs free energy (ΔG*H) of the S-scheme heterojunction in the composite material is -0.07 eV, which is close to 0. This promotes the adsorption of H* and accelerates the formation of H2. Internal photothermal catalysis is achieved by visible-near infrared (Vis-NIR, RT) irradiation. The internal photothermal catalytic hydrogen production rate of the best sample (0.9Ni-NiO@CNFs/ZIS-Vs) is as high as 17.24 mmol·g-1·h-1, and its photothermal conversion efficiency (η) is as high as 61.42 %. Its hydrogen production efficiency is 20.52 times that of ZIS-Vs (0.84 mmol·g-1·h-1) under visible light (Vis, RT) conditions. When the Vis-NIR light source is combined with external heating (75 ℃), the hydrogen production efficiency is further improved, and the hydrogen production efficiency (29.16 mmol·g-1·h-1) is 26.75 times that of ZIS-Vs (1.09 mmol·g-1·h-1, Vis-NIR, RT). Further analysis shows that the increase in hydrogen production resulted from the apparent activation energy (Ea) of the catalyst decreasing from 16.7 kJ·mol-1 to 9.28 kJ·mol-1. This study provides a valuable prototype for the design of an efficient photothermal synergistic catalytic system.
Keywords: Hydrogen evolution; Ni-NiO@CNFs; Photothermal conversion effect; Photothermal synergistic catalysis; ZnIn(2)S(4).
Copyright © 2024 Elsevier Inc. All rights reserved.