Effects of Printing Angle and Post-Curing Time on the Color and Translucency of 3D-Printed Temporary Restoration

Biomimetics (Basel). 2024 Jul 10;9(7):420. doi: 10.3390/biomimetics9070420.

Abstract

In resins produced with a 3D printer, the printing parameters affect the properties of the restoration produced. This study examined the effect of the printing angle and post-curing time on the optical properties of temporary restorations. A total of 135 disk-shaped Formlabs temporary resins (10 × 2 mm) were produced at three different printing angles (0, 45, and 90 degrees) and post-cured for three different times (20, 40, and 60 min) (n = 15). Color and translucency measurements were taken for each group with a spectrophotometer (VITA Easyshade V). The ΔE values between printing angles and curing times influence each other. The highest color change was observed in the groups produced with a 90° printing angle. Considering the post-curing times, the highest color change was observed in the groups cured for 40 min. Increasing the curing time from 20 to 40 min decreases the translucency, whereas further increasing the curing time does not significantly affect the translucency. In terms of the impact on the translucency caused by the printing angles, 0° exhibited a lower translucency compared to other printing angles. During the 3D printing of temporary prostheses, both printing angles and post-curing times can affect their optical properties.

Keywords: 3D printing; post-curing time; printing angle.

Grants and funding

This research received no external funding.