Dy3+ -doped Y3 Al5 O12 phosphors were prepared at a relatively low temperature using molten salt synthesis. The phase of the prepared Dy3+ -doped Y3 Al5 O12 phosphors was confirmed using X-ray powder diffraction. Results indicated that Dy3+ doping did not change the Y3 Al5 O12 phase. Following excitation at 352 nm, emission spectra of the Dy3+ -doped Y3 Al5 O12 phosphors consisted of blue, yellow, and red emission bands. The influence of Dy3+ concentration and excitation wavelength on emission was investigated. The ratio of yellow light to blue light varied with change in Dy3+ doping concentration, due to changes in the structure around Dy3+ . Emission intensities also changed when the excitation wavelength was changed. This variation is luminescence generated a system for tunable white light for Dy3+ -doped Y3 Al5 O12 phosphors.
Keywords: Y3Al5O12:Dy3+; molten salt synthesis; white light.