A novel core-shell Fe3O4@FeS composed of Fe3O4 core and FeS shell with the morphology of regular octahedra has been prepared via a facile and scalable strategy via employing commercial Fe3O4 as the precursor. When used as anode material for sodium-ion batteries (SIBs), the prepared Fe3O4@FeS combines the merits of FeS and Fe3O4 with high Na-storage capacity and superior cycling stability, respectively. The optimized Fe3O4@FeS electrode shows ultralong cycle life and outstanding rate capability. For instance, it remains a capacity retention of 90.8% with a reversible capacity of 169 mAh g-1 after 750 cycles at 0.2 A g-1 and 151 mAh g-1 at a high current density of 2 A g-1, which is about 7.5 times in comparison to the Na-storage capacity of commercial Fe3O4. More importantly, the prepared Fe3O4@FeS also exhibits excellent full-cell performance. The assembled Fe3O4@FeS//Na3V2(PO4)2O2F sodium-ion full battery gives a reversible capacity of 157 mAh g-1 after 50 cycles at 0.5 A g-1 with a capacity retention of 92.3% and the Coulombic efficiency of around 100%, demonstrating its applicability for sodium-ion full batteries as a promising anode. Furthermore, it is also disclosed that such superior electrochemical properties can be attributed to the pseudocapacitive behavior of FeS shell as demonstrated by the kinetics studies as well as the core-shell structure. In view of the large-scale availability of commercial precursor and ease of preparation, this study provide a scalable strategy to develop advanced anode materials for SIBs.
Keywords: Fe3O4; anode materials; full cell; scalable preparation; sodium-ion batteries.