In this work, carbon black (CB)/polyamide 6 (PA6)/polypropylene (PP) microfibrillar composites (MFCs) were fabricated through an extrusion (hot stretching) heat treatment process. The CB-coated conductive PA6 microfibrils with high aspect ratio were in situ generated as a result of the selective accumulation of CB at the interface. At the proper temperature, a 3D entangled conductive structure was constructed in the PP matrix, due to topological entanglement between these conductive microfibrils. This unique conductive structure provided the PP composites with a low electrical conductivity percolation threshold. Moreover, the electromechanical properties of conductive MFCs were investigated for the first time. A great stability, a high sensitivity and a nice reproducibility were achieved simultaneously for CB/PA6/PP MFCs. This work provides a universal and low-cost method for the conductive polymer composites' (CPCs) fabrication as sensing materials.
Keywords: conductive structure; electromechanical property; microfibrillar composites (MFCs); sensing.