The development of a flexible and high-performance humidity sensor is essential to expand its new applications, such as personal health monitoring and early diagnosis. In this work, SnO2/rGO nanocomposites were prepared by one-step hydrothermal method. The effect of rGO-doping on humidity sensing performance was investigated. Scanning electron microscopy, transmission electron microscopy, X-ray diffraction and Raman spectroscopy were used to characterize the nanostructure, morphology and chemical composition of SnO2/rGO nanocomposites. The SnO2/rGO humidity sensitive film was prepared by electrospinning on a polyimide film modified with gold electrodes. The humidity test results show that different doping ratios of rGO have different effects on humidity sensing properties. Among them, the sensor with 2 wt% rGO-doping has a high sensitivity (37,491.2%) within the humidity range as well as the fast response time (80 s) and recover time (4 s). Furthermore, the sensor with 2 wt% rGO-doping remains good flexibility and stability in the case of bending (1000 times). The sensitivity of the 2 wt% rGO-doping sensor at the bending radius (8 mm and 4 mm) is 48,219% and 91,898%, respectively. More importantly, the sensor could reflect different breathing states clearly and track breathing intervals as short as 3 s. The SnO2/rGO flexible humidity sensor with accuracy, flexibility and instantaneity as well as the facile fabrication strategy is conceivable to be applied in the potential application for human health real-time monitoring.
Keywords: SnO2/rGO nanocomposite; breath monitoring; flexibility; humidity sensor.