Pectin has excellent film-forming properties, but its functional properties need to be enhanced. Therefore, we constructed naturally branched phytoglycogen (PG) nanoparticles to solubilize curcumin (CCM) and further enhance the properties of apple pectin-based active films. The size of the PG spherical particles ranged from 30 to 100 nm with some aggregates. The branch density of the PG was 6.02 %. These PG nanoparticles increased the solubility of CCM nearly 1742-fold and a nanosized phytoglycogen-curcumin (PG-CCM) host was formed via hydrogen bonding and hydrophobic interaction. This host promoted the formation of pectin-based films with a dense structure and increased their tensile strength to 23.51 MPa. The coefficient to water vapor permeability, oxygen permeability and carbon dioxide permeability were all decreased indicating their barrier performance were improved. Among them, the oxygen permeability coefficient decreased most, from 1.14 × 10-7 g·m-1·s-1 to 0.8 × 10-7 g·m-1·s-1. Also, the transmittance of the active film at 280 nm and 660 nm decreased to 0.65 % and 72.10 %. Antioxidant and antibacterial properties were significantly enhanced (P < 0.05). And the results showed this film was an excellent oil packaging material. The active film incorporating PG-CCM host can replace heat-sealed plastic bags/pouch made from polyethylene and polypropylene synthetic plastics, and solve the problem that plastic packaging is difficult to degrade and cannot be squeezed clean. This provides a new conceptual framework for developing pectin-based active films by incorporating of PG and CCM.
Keywords: Active films; Curcumin; Oil preservation; Pectin; Phytoglycogen.
Copyright © 2024 Elsevier B.V. All rights reserved.