Engineering a Low-Strain Si@TiSi2@NC Composite for High-Performance Lithium-Ion Batteries.
Zhang W, Li W, Gui S, Wang X, Zhang Z, Chen Q, Wei J, Tu S, Duan X, Wang X, Cheng K, Zhan R, Tan Y, Fan F, Zhang Y, Li H, Sun Y, Zhou H, Yang H.
Zhang W, et al. Among authors: cheng k.
ACS Appl Mater Interfaces. 2024 May 7. doi: 10.1021/acsami.4c03759. Online ahead of print.
ACS Appl Mater Interfaces. 2024.
PMID: 38711193
As a result, the as-fabricated Si@TiSi(2)@NC electrode exhibits a high initial reversible capacity (2172.7 mAh g(-1) at 0.2 A g(-1)), superior rate performance (1198.4 mAh g(-1) at 2.0 A g(-1)), and excellent long-term cycling stability (847.0 mAh g(-1) after 1000 cycles a …